SURFACE MICROHARDNESS OF MICROHYBRID AND NANOCOMPOSITE AFTER STORAGE IN MOUTH WASHES
DOI:
https://doi.org/10.55519/JAMC-03-10181Keywords:
Resin composites, Mouthwashes, Microhardness, Microhybrid composite, Hardness testAbstract
Background: Dental composites are aesthetic direct restorative material. However, the effect of mouthwashes on the durability of the material is controversial. This study evaluated and compared the influence of mouthwash composition on the surface hardness of nanofilled (Z350XT) and microhybrid (P60) resin composites. Methods: Comparative in-vitro study was conducted over 6 months at Multan Medical & Dental College. Sixty-four disc-shape specimens of each {nanofilled (Z350XT) and microhybrid (P60)} resin composite were prepared and stored in distilled water at 37°C for 24 hours. The baseline microhardness reading (To) was recorded by Vickers micro-hardness tester. Samples were then randomly divided into four groups (n=16) and stored in Listerine Cool Mint, Colgate Plax, Clinica and distilled water (control). The hardness test was repeated after 12 hours and 24 hours of storage. Results: Nanocomposite (Z350XT) had statistically (p<0.01) higher surface hardness. A significant reduction (p‰¤0.05) in microhardness was observed after immersion of samples in mouthwashes. The reduction in surface hardness was dependent on the immersion time and composition of mouthwashes. Listerine Cool Mint (alcohol-based mouthwash) had greatest degradation effect. Conclusion: Mouth rinses negatively impacted the surface microhardness of the tested resin-based materials. Alcohol-based mouthwashes had greater potential for reducing microhardness. Microhybrid composite appears to be a more suitable material for restoring teeth in patients accustomed to using regular mouthwashes.
References
Alzraikat H, Burrow M, Maghaireh G, Taha N. Nanofilled resin composite properties and clinical performance: a review. Oper Dent. 2018;43(4):E173-E90.
da Silva E, de Sá Rodrigues C, Dias D, da Silva S, Amaral C, Guimarães J. Effect of Toothbrushing-mouthrinse-cycling on Surface Roughness and Topography of Nanofilled, Microfilled, and Microhybrid Resin Composites. Oper Dent. 2014;39(5):521-9.
Ozer S, Sen Tunc E, Tuloglu N, Bayrak S. Solubility of two resin composites in different mouthrinses. Biomed Res Int. 2014:580675. doi: 10.1155/2014/580675.
Randolph LD, Palin WM, Leloup G, Leprince JG. Filler characteristics of modern dental resin composites and their influence on physico-mechanical properties. Dent Mater. 2016;32(12):1586-99.
Poggio C, Viola M, Mirando M, Chiesa M, Beltrami R, Colombo M. Microhardness of different esthetic restorative materials: Evaluation and comparison after exposure to acidic drink. Dent Res J (Isfahan). 2018;15(3):166-72.
Cao L, Zhao X, Gong X, Zhao S. An in vitro investigation of wear resistance and hardness of composite resins. Int J Clin Exp Med. 2013;6(6):423-30.
Festuccia MSCC, Garcia LdFR, Cruvinel DR, Pires-De-Souza FdC. Color stability, surface roughness and microhardness of composites submitted to mouthrinsing action. J Appl Oral Sci. 2012;20(2):200-5.
Koshhar R, Dewan R, Soi S, Punjabi M. An evaluation and comparison of the effect of five mouthrinses on the microhardness of esthetic hybrid composite restorative-material-an in vitro study. J Dent Specialities. 2017;5:66-9.
Jyothi K, Crasta S, Venugopal P. Effect of five commercial mouth rinses on the microhardness of a nanofilled resin composite restorative material: An in vitro study. J Conserv Dent. 2012;15(3):214.
Miranda DdA, Bertoldo CEdS, Aguiar FHB, Lima DANL, Lovadino JR. Effects of mouthwashes on Knoop hardness and surface roughness of dental composites after different immersion times. Brazil Oral Res. 2011;25(2):168-73.
Diab M, Zaazou M, Mubarak E, Olaa M. Effect of five commercial mouthrinses on the microhardness and color stability of two resin composite restorative materials. Aust J Basic Appl Sci. 2007;1(4):667-74.
Wataha JC, Lewis J, Lockwood P, Hsu S, Messer R, Rueggeberg F, et al. Blue light differentially modulates cell survival and growth. J Dent Research. 2004;83(2):104-8.
Casanova Obando PE, Taboada Alvear MF, Flores Cuvi DS, Castilla M, Armas AdC. Effect of three mouthrinses on surface degradation of resin composite: in vitro study. Revista de OdontopediatrÃa Latinoamericana. 2020;8(2):141-53.
Rajasekhar R, James B, Johny MK, Jacob J. Evaluation of the effect of two commercially available non-alcoholic mouth rinses on the microhardness of composite material-An invitro study. Dent J. 2019; 1(1):14-21
Das S, Sowmya K. An evaluation of the effect of alcohol and non-alcohol based mouth rinses on the microhardness of two esthetic restorative materials-An in vitro study. Int J Appl Dent Sci. 2015;1:27-31.
Nowak M, Kalamarz I, Chladek G. Mechanical properties of Easy Fill composites after storage in mouthwashes. J Achiev Mater Manuf Eng. 2018;88(1):25-31
Goyal DA, George DJV, Mathew DS, Singh DR, Ramesh D, editors. Effect of four commercial mouth rinses on the microhardness and solubility of a supra nanocomposite and a microhybrid composite: An in vitro study2016.
Dash S, Kallepalli S. An evaluation of the effect of Alcohol and Non-Alcohol based mouth rinses on the microhardness of two esthetic restorative materials-An in vitro Study. Int J Appl Dent Sci. 2015;1(2):27-31.
de Moraes PI, das Neves L, de Souza C, Parolia A, Barbosa DSN. A comparative effect of mouthwashes with different alcohol concentrations on surface hardness, sorption and solubility of composite resins. Oral Health Dent Manag. 2014;13(2):502-6.
Downloads
Published
How to Cite
Issue
Section
License
Journal of Ayub Medical College, Abbottabad is an OPEN ACCESS JOURNAL which means that all content is FREELY available without charge to all users whether registered with the journal or not. The work published by J Ayub Med Coll Abbottabad is licensed and distributed under the creative commons License CC BY ND Attribution-NoDerivs. Material printed in this journal is OPEN to access, and are FREE for use in academic and research work with proper citation. J Ayub Med Coll Abbottabad accepts only original material for publication with the understanding that except for abstracts, no part of the data has been published or will be submitted for publication elsewhere before appearing in J Ayub Med Coll Abbottabad. The Editorial Board of J Ayub Med Coll Abbottabad makes every effort to ensure the accuracy and authenticity of material printed in J Ayub Med Coll Abbottabad. However, conclusions and statements expressed are views of the authors and do not reflect the opinion/policy of J Ayub Med Coll Abbottabad or the Editorial Board.
USERS are allowed to read, download, copy, distribute, print, search, or link to the full texts of the articles, or use them for any other lawful purpose, without asking prior permission from the publisher or the author. This is in accordance with the BOAI definition of open access.
AUTHORS retain the rights of free downloading/unlimited e-print of full text and sharing/disseminating the article without any restriction, by any means including twitter, scholarly collaboration networks such as ResearchGate, Academia.eu, and social media sites such as Twitter, LinkedIn, Google Scholar and any other professional or academic networking site.